Characterization of nano bamboo charcoal drug delivery system for Eucommia ulmoides extract and its anticancer effect In vitro
Zhaoyan Zeng1, Xiangzhou Li2, Sheng Zhang1, Dan Huang3
1 Department of Chemical Engineering, College of Materials Science and Engineering, Central South University of Forestry and Technology, Changsha 410004, China
2 Department of Chemical Engineering, College of Materials Science and Engineering, Central South University of Forestry and Technology, Changsha 410004; State Key Laboratory of Ecological Applied Technology in Forest Area of South China, Changsha 410004, China
3 State Key Laboratory of Chinese Medicine Powder and Medicine Innovation in Hunan (Incubation), Hunan University of Chinese Medicine, Changsha 410208, China
|Date of Submission||27-May-2016|
|Date of Acceptance||11-Jul-2016|
|Date of Web Publication||19-Jul-2017|
State Key Laboratory of Ecological Applied Technology in Forest Area of South China, Changsha 410004
Source of Support: None, Conflict of Interest: None
| Abstract|| |
Background: Nano bamboo charcoal is being widely used as sustained release carrier for chemicals for its high specific surface area, sound biocompatibility, and nontoxicity; however, there have been no reports on nano bamboo charcoal as sustained release carrier for traditional Chinese medicine (TCM). Objective: To study the effect of nano bamboo charcoal in absorbing and sustained releasing Eucommia ulmoides extract (EUE) and to verify the in vitro anticancer effect of the sustained release liquid, so as to provide a theoretical basis for the development and utilization of nano bamboo charcoal as TCM sustained-release preparation. Materials and Methods: The adsorption capacity for the nano bamboo charcoal on EUE was measured by Langmuir model, and the release experiment was carried out under intestinal fluid condition. Characteristic changes for the nano bamboo charcoal nano-drug delivery system with and without adsorption of E. ulmoides were evaluated by scanning electron microscopy, Fourier transform infrared spectroscopy, thermogravimetric analysis, and specific surface area. In addition, the anticancer effect from this novel bamboo charcoal E. ulmoides delivery system was evaluated against a human colon cancer cell line (HCT116). Results: It was found that nano bamboo charcoal exhibits good adsorption capacity (up to 462.96 mg/g at 37°C). The cumulative release rate for EUE from this nano bamboo charcoal delivery system was 70.67%, and specific surface area for the nano bamboo charcoal decreased from 820.32 m2/g to 443.80 m2/g after EUE was loaded. An in vitro anticancer study showed that the inhibition rate for E. ulmoides against HCT116 cancer cells was 23.07%, for this novel bamboo charcoal nano-drug delivery system. Conclusion: This study provides a novel strategy for the delivery of traditional Chinese medicine using bamboo charcoal nano-drug delivery system.
Abbreviation used: EUE: Eucommia ulmoides extract.
Keywords: Adsorption, anticancer effect, Eucommia ulmoides extract, nano bamboo charcoal, sustained release
|How to cite this article:|
Zeng Z, Li X, Zhang S, Huang D. Characterization of nano bamboo charcoal drug delivery system for Eucommia ulmoides extract and its anticancer effect In vitro. Phcog Mag 2017;13:498-503
|How to cite this URL:|
Zeng Z, Li X, Zhang S, Huang D. Characterization of nano bamboo charcoal drug delivery system for Eucommia ulmoides extract and its anticancer effect In vitro. Phcog Mag [serial online] 2017 [cited 2022 Jan 24];13:498-503. Available from: http://www.phcog.com/text.asp?2017/13/51/498/211025
- The adsorption equilibrium was reached after 30 min of ultrasonic treatment
- The saturated adsorption capacity of Eucommia ulmoides extract by nano bamboo charcoal under ultrosonic condition was 462. 96 mg/g
| Introduction|| |
Eucommia ulmoides Oliv. (From Eucommiaceae family) is the sole species of the genus Eucommia that has been used as a rare tonic Chinese herbal medicine for nearly 2000 years. Multiple pharmacological activities of E. ulmoides have been reported including lowering of blood pressure and improvement of immunity, as well as anti-inflammatory, antiviral, anticancer, hepatic protection, and diuretic effects. In addition, antioxidation and antiaging effects of E. ulmoides have also been observed.,,,E. ulmoides has also been processed into Eucommia tea and Eucommia vinegar beverages.
Nano bamboo charcoal is widely used as a multifunctional material because of its high mechanical strength, well-developed pore structure, and excellent adsorptive property. The nano bamboo charcoal has been recently developed and used as a sustained release carrier in the pharmaceutical area., The nano bamboo charcoal has a large specific surface area and high adsorptive capacity when compared with other drug delivery carriers. It also has the capacity to adsorb a wide variety of drugs without affecting their molecular properties; hence, it is regarded as an ideal drug delivery carrier.,, There are currently some concerns that large amount of drugs may be unexpectedly released from drug delivery systems in a very short period of time, which may rapidly increase the in vivo blood concentration as a result, possibly leading to adverse reactions. There is, therefore, an urgent need for developing the drug carrier system with sustained-releasing effect.
In the current study, E. ulmoides extract (EUE) was loaded into the nano bamboo charcoal which was used as the drug delivery carrier. The characteristics for the prepared nano bamboo charcoal delivery system were also evaluated in this study, including adsorption and release of Eucommia extract from the delivery system. The adsorption capacity for the nano bamboo charcoal to adsorb EUE was characterized by a combination of methods including scanning electron microscopy (SEM), Fourier transform infrared (FT-IR) spectroscopy, thermogravimetric (TG) analysis, and specific surface area (Brunauer–Emmett–Teller [BET]). We also investigated the in vitro, anticancer effect of nano bamboo charcoal as the sustained release carrier for EUE.
| Materials and Methods|| |
Nano bamboo charcoal (with a mean diameter of 100 nm) was purchased from Shanghai Hairuo Charcoal Industry Co. Ltd. (Shanghai, China). EUE was purchased from Hunan Yuanhang Biological Technology Co. Ltd. (Hunan, China).
Fetal bovine serum and 0.25% trypsin were purchased from GIBCO (California, USA). Myllicin double antibody was purchased from CHINO Pharmaceutical Co. Ltd. (Shijiazhuang, China). Modified RPMI-1640 culture medium was obtained from Hyclone (Los Angeles, America). Phosphate-buffered saline was purchased from Hyclone. 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) and dimethyl sulfoxide were purchased from Sigma (USA) and American Ameresco, respectively. HCT116 cell line was generously donated by Prof. Ying-Liang from National Engineering Laboratory for Further Processing of Grains of Central South University of Forestry and Technology. All other chemicals and solvents were of analytical or chromatographic grade.
Characterization of nano bamboo charcoal drug delivery system for adsorption and release
EUE solutions were prepared using distilled water (pH 7.4) at 0.05 mg/L and 0.1 mg/L concentrations, followed then by their scanning at 200–600 nm wavelength range, with distilled water being used as a blank. Results showed that EUE exhibited a maximum adsorption at the 280 nm and 326 nm wavelengths. Three hundred and twenty-six nanometers was chosen as detection wavelength because of the observed stable adsorption.
Standard curve for Eucommia ulmoides extract
EUE was dissolved in distilled water at the following standard concentrations 40, 50, 60, 80, 100, and 120 mg/L. The ultraviolet (UV) absorbance for standard solutions with different concentrations was determined at 326 nm wavelength using the distilled water as a blank. Linear regression for the concentration (C) against the absorbance (D) was plotted.
Determination of adsorption equilibrium time
A volume of 600 mg/L EUE solution was added into 0.1 g nano bamboo charcoal, and the suspension was then ultrasonically oscillated for 6, 12, 18, 24, 30, and 36 min. The supernatant absorbance at appropriate dilution time was then measured at 326 nm. The concentration of EUE in the supernatant was then calculated using the regression equation for the standard curve. The adsorption capacity (X) for the nano bamboo charcoal was determined as follows:
where C0represented the initial concentration ofEUE; C represented the supernatant concentration for EUE after centrifugation; m represented the amount of added nano bamboo charcoal; and v represented the solvent volume.
Determination of adsorption capacity of nano bamboo charcoal on
Eucommia ulmoides extract
However, assessing the adsorption capacity of nano bamboo charcoal loaded with EUE is critical. Prepared solutions of EUE at 500, 550, 600, 650, 700, and 800 mg/L concentrations were added into 1% (m/v) nano bamboo charcoal. The adsorption equilibrium was completed after ultrasonic oscillation for 30 min. The suspensions were then centrifuged at 7800 g for 5 min, and the UV adsorbance ofEUE in the diluted supernatant was measured at 326 nm. The Langmuir adsorption calibration curve for C/X versus C was then plotted as follows;
where C represented free EUE concentration after equilibrium; X represented the adsorptive capacity for the nano bamboo charcoal on EUE; K represented the Langmuir equilibrium parameter; and Xm represented the maximum adsorption capacity.
Evaluation of retention release for prepared nano bamboo charcoal drug delivery system
The release of EUE was carried out as follows: 500 mg/g (weight of EUE [mg/L]/weight of nano bamboo charcoal [g]) nano bamboo charcoal formulation was prepared as previously described. Briefly, 500 mg of EUE was added into 1 g of nano bamboo charcoal, and the mixture was then ultrasonically oscillated to reach adsorption equilibrium. A dried solid dispersion was obtained after removal of the supernatant, and 0.1 g of the above solid dispersion was then dispensed by stirring in 200 mL of simulated intestinal fluid at 37°C. Five milliliters of the suspension was then drawn and filtered through 0.45 μm membrane filter. A total volume of 200 mL was kept constant by adding 5 mL of blank simulated intestinal fluid after each sampling. EUE in the released solution was determined by UV–visible. The percent release capacity Q (%) was calculated as follows;
where Q (%) is the cumulative release rate of EUE, Cn(mmol/L) is the concentration of EUE after the n-th sampling, V0(mL) is the total volume ofEUE solution, Vi(mL) is the sampling volume, Ci(mmol/L) is the concentration of EUE at the i-th sampling, whereas m(g) means the mass of solid dispersion. The cumulative release rate was then calculated, and the drug release curve drawn using Higuchi regression.
Physical and structural characterization of nano bamboo charcoal drug delivery system
Morphological changes in the nano bamboo charcoal before and after adsorption were observed using a SEM (FEI Quanta 450, USA). Images were taken without prior treatment to ensure the acquisition of accurate images. The surface area and the pore size distribution were calculated according to BET and Barrett–Joyner–Halenda method (Kurt SA3100, USA). The weight loss of the nano bamboo charcoal before and after adsorption was determined by Pyris 1 TG/derivative thermogram (TG/DTG) analyzer using N2 as protective gas, 40 mL/min flow rate, and 10°C/min temperature rising speed. The initial and terminal temperatures were set at 25°C and 800°C, respectively, and the sample weight was about 8 mg. The functional groups of the nano bamboo charcoal before and after adsorption were investigated with a FT-IR spectroscopy (IRAffinity-1, Shimadzu Corp., Japan).
Cytotoxicity effect of nano bamboo charcoal drug delivery system on colon cancer cell line HCT116
The cytotoxicity of the released solutions from the prepared nano bamboo charcoal drug delivery system at different time points against the colon cancer cell line HCT116 was evaluated using MTT assay.
| Results and Discussion|| |
Nano bamboo charcoal adsorption performance
A standard curve for EUE was made as depicted in [Figure 1]a. A good correlation (D = 0.00718C-0.05207; R2 = 0.9997, P< 0.0001) between the measured UV adsorption at 326 nm (D326) and EUE concentration (C) was observed from 40 to 120 mg/L range., Next adsorption equilibrium time was explored. From [Figure 1]b, it can be observed that the adsorption capacity Xm for EUE increases with increasing ultrasonic time of EUE. This can be attributed to the accelerated diffusion of EUE molecules onto nano bamboo charcoal by the increase ultrasonic time of EUE. Respectively, the adsorbed amounts ofEUE were (326.47 ± 8.62) mg/g, (369.82 ± 7.21) mg/g, (412.83 ± 6.24) mg/g, (441.61 ± 9.86) mg/g, (454.63 ± 10.11) mg/g, and (454.88 ± 10.86) mg/g at 6, 12, 18, 24, 30, and 36 min. The maximum adsorption capacity of EUE is 454.88 mg/g around 36 min, which indicated that the adsorption equilibrium was reached after 30 min of ultrasonic treatment.
|Figure 1: (a and b) Adsorption of Eucommia ulmoides extract (X [mg/g]) by nano bamboo charcoal at different ultrasonic time intervals (T [min]); (c) Adsorption isotherm curve for nano bamboo charcoal drug delivery system. The isotherm data fit the Langmuir and model (Y = 0.00216X + 0.0216, r = 0.9996, P < 0.0001); (d) Cumulative release rate of nano bamboo charcoal drug delivery system. Release in vitro of nano bamboo charcoal drug delivery system accorded with Higuchi model|
Click here to view
The parameters of nano bamboo charcoal were extracted from the effect of initial EUE concentration on adsorption capacity [Figure 1]c. The data were obtained by fitting Langmuir. The Langmuir model assumes that the binding sites are homogeneously distributed over the adsorbent surface with monolayer coverage and uniform energies. A correlation (Y = 0.00216X + 0.0216; R2 = 0.9994, P< 0.0001) between the free EUE concentration after equilibrium (C) and adsorptive capacity of nano bamboo charcoal. According to the Correlation coefficient (R2), it can be concluded that the Langmuir model fits the equilibrium data. Indicating that adsorption is highly favorable for nano bamboo charcoal. According to Langmuir model, Xm was determined as 462. 96 mg/g, indicating that 1 g of nano bamboo charcoal was able to adsorb 462.96 mg of EUE after reaching the adsorption equilibrium. In other words, the maximum mass ratio between the adsorbed EUE and nano bamboo charcoal was 1:2. These results indicate that the high adsorptive capacity for the nano bamboo charcoal as the drug carrier.
Nano bamboo charcoal release performance
[Figure 1]d shows the cumulative release rate for nano bamboo charcoal drug delivery system. From this [Figure 1]d, we can see that nearly 71% of EUE adsorbed by nano bamboo charcoal is released. A fast release of EUE can be observed within the initial 60 min, followed by a slow increase of concentration before reaching the plateau at 3 h. The drug releasing rate is relatively higher during the initial releasing period (<1 h), which indicates the occurrence of initial burst release. Furthermore, EUE near the entrance and on the surface of the nano bamboo charcoal diffuse into dissolution medium easily. In addition, EUE was loaded by physical adsorption which is a reversible process. Release will occur more easily in the dissolution medium. Moreover, the release in vitro of nano bamboo charcoal drug delivery system complied with Higuchi model. It shows that the release of EUE from artificial intestinal juice is controlled by a diffusion mechanism.
Surface morphology of nano bamboo charcoal drug delivery system
The surface morphology of the nano bamboo charcoal before and after adsorption was observed using the SEM as shown in [Figure 2]. It can be seen that the surface of the nano bamboo charcoal was smooth and square [Figure 2]a, which can realize the homogeneity of the drug distribution. Hence, it was extremely helpful for calculating accurately the drug loading and drug release. However, for the nano bamboo charcoal after adsorption [Figure 2]b, the surface of it was covered by EUE. Moreover, a much lighter surface of the nano bamboo charcoal was observed after the adsorption, which may have been due to poor conductivity caused by the attachment of chlorogenic acid, geniposide, gensipodic acid, and other low-conductivity components from EUE. These findings suggested that EUE was successfully loaded onto the nano bamboo charcoal.
|Figure 2: Scanning electron microscopy image of nano bamboo charcoal before (a) and after (b) adsorption|
Click here to view
Chemical and structural properties of nano bamboo charcoal drug delivery system
Brunauer–Emmett–Teller and pore size distribution analysis
According to the IUPAC classification, as seen in [Figure 3], the N2 adsorption isotherms of the nano bamboo charcoal before [Figure 3]a and after [Figure 3]b adsorptions indicated a Type I isotherm. The detailed data about the nano bamboo charcoal before and after adsorptions resulting from the N2 adsorption are summarized in [Table 1]. It can be seen that the nano bamboo charcoal had large BET surface area (820.32 m2/g) and pore volume (0.4833 mL/) which was sufficiently large to load EUE molecules. With these extraordinary advantages, nano bamboo charcoal as a drug carrier can disperse EUE particles effectively and also prevent agglomeration. Furthermore, the BET surface area and pore volume were sharply reduced after nano bamboo charcoal had been loaded. The total specific surface area decreased to 443.80 m2/g, and total pore volume also decreased to 0.2885 mL/g, suggesting that EUE was adsorbed onto the surface or inner structure of the charcoal and resulting in the decrease of both total surface area and total pore volume.
|Figure 3: N2 adsorption curve of nano bamboo charcoal before (a) and after (b) adsorption|
Click here to view
|Table 1: Specific surface area and pore structure parameters of nano bamboo charcoal|
Click here to view
The TG/DTG result of the nano bamboo charcoal before [Figure 4]a and after [Figure 4]b adsorption was shown in [Figure 4]. A three-phase thermal decomposition was observed before adsorption, according to the TG/DTG diagram. The weight loss of the first stage (40°C–100°C) is primarily due to water evaporation. The second stage involved 100°C–400°C temperature range, with flat thermal decomposition curve indicating that there was no thermal decomposition and weight loss for the nano bamboo charcoal in this phase. The weight of the nano bamboo charcoal fell from 77% to 20% in the third stage, from 400°C to 800°C.
|Figure 4: Derivative thermogram-thermogravimetric curves for nano bamboo charcoal before (a) and after (b) Eucommia ulmoides extract adsorption|
Click here to view
Four phases of thermal decomposition for the nano bamboo charcoal were found after loading of EUE. Lower weight loss was observed in the first phase (from 40°C to 100°C) since the loaded EUE may also have broken down, leading to the slow decomposition rate as demonstrated by the DTG curve. The second phase was from 100°C to 200°C temperature range, in which no weight loss was observed. Significant thermal decomposition was observed at 200°C–380°C range in the third phase at which there was no decomposition for the nano bamboo charcoal before adsorption, and therefore, such unique decomposition was due to the adsorption of E. ulmoides components. Chlorogenic acid has been proven, by HPLC analysis, to be a major component of EUE whose thermal decomposition characteristics were reported to be in accordance with our present findings. The fourth stage was from 380°C to 800°C temperature range, and the gradual decomposition manner was consistent with those for the nano bamboo charcoal and chlorogenic acid. In summary, these observations further supported the findings that EUE was adsorbed by the nano bamboo charcoal.
The FT-IR spectrum, as shown in [Figure 5], was collected to investigate the chemical bonds of the nano bamboo charcoal drug delivery system. Infrared analyses of nano bamboo charcoal before and after adsorption [Figure 5]a and EUE [Figure 5]b. The broad absorption band at 3600–3000 cm−1 with a maximum at about 3382 cm−1 is characteristic of the stretching vibration of hydrogen-bonded hydroxyl groups from carboxyls, phenols, or alcohols, and water adsorbed in the nano bamboo charcoal. The weak absorption peaks at 2904 cm−1 and 2837 cm−1 were characteristic for -CH3. Peaks at 1573 cm−1 and 1242 cm−1 were specific carboxylic acid absorption peaks, whereas the peaks at 1066 cm−1 may have been caused by C-O stretching vibration of ether., The new absorption peaks at 3382 cm−1 and 667 cm−1 were observed during loading of EUE. Moreover, the peak absorptions at 1573 cm−1, 1240 cm−1, and 1066 cm−1 were enhanced after loading of EUE. In addition, the inverted peaks at 1450 cm−1 and 1108 cm−1 appeared in the prepared formulation. When compared with the IR spectra form the nano bamboo charcoal before the adsorption, the prepared formulation showed peaks at 1633 cm−1, 1527 cm−1, 1274 cm−1, and 688 cm−1, which are characteristic IR adsorption peaks for benzene derivatives in Eucommia extract, indicating that EUE was successfully loaded.
|Figure 5: Infrared spectra from nano bamboo charcoal before (a) and after (b) adsorption of Eucommia ulmoides extract|
Click here to view
Cytotoxic effect of nano bamboo charcoal drug delivery system on colon cancer cell line HCT116
The inhibitory effect of the nano bamboo charcoal drug delivery system on the colon cancer cell line HCT116 is shown in [Table 2]. It was found that the inhibitory effect of the releasedEUE increased accordingly with increased release time. A maximum inhibitory effect of 23.07% on the HCT116 cancer cells was observed after 3 h release. These results showed that the prepared novel drug delivery system had an obvious inhibitory effect on the HCT116 cancer cells.
|Table 2: Cytotoxic effect of nano bamboo charcoal drug delivery system on colon cancer cell line HCT116|
Click here to view
| Conclusions|| |
In summary, the current study successfully prepared a novel and sustained release nano bamboo charcoal drug delivery system for EUE. The adsorption experiment shows that nano bamboo charcoal exhibits an excellent adsorption capacity (up to 462.96 mg/g at 37°C). The nano bamboo charcoal drug delivery system can be well described by Langmuir and Higuchi model. Physical and chemical properties and structure analysis confirm that the specific surface area, surface morphology, and functional groups in nano bamboo charcoal drug delivery system, verifying their good adsorption and release behavior. Cell in vitro study demonstrated the significant anticancer effect of this novel drug delivery system. This is the first application of the nano bamboo charcoal drug delivery system to well-known traditional Chinese medicine (TCM) of E. ulmoides, which provides a new strategy of oral delivery of TCM. Therefore, nano bamboo charcoal would have enormous potential applications for drug delivery systems in the future. Nevertheless, future challenges remain, including improving specificity and stability and regulating bioavailability.
Financial support and sponsorship
The authors would like to acknowledge supports from Fund of the Natural Science Foundation of Hunan province (2015JJ2196) and National Key Technology R&D Program in the 12th Five Year Plan of R. P. China (2012BAD21B05).
Conflicts of interest
There are no conflicts of interest.
| References|| |
Wang DW, Li Y, Li ZQ. Identification of a male-specific Amplified Fragment Length Polymorphism (AFLP) and a Sequence Characterized Amplified Region (SCAR) marker in Eucommia ulmoides
Oliv. Int J Mol Sci 2011;12:857-64.
Ding Y, Dou D, Guo Y, Li Q. Simultaneous quantification of eleven bioactive components of male flowers of Eucommia ulmoides
Oliver by HPLC and their quality evaluation by chemical fingerprint analysis with hierarchical clustering analysis. Pharmacogn Mag 2014;10:435-40.
He X, Wang J, Li M, Hao D, Yang Y, Zhang C, et al. Eucommia ulmoides
Oliv.: Ethnopharmacology, phytochemistry and pharmacology of an important traditional Chinese medicine. J Ethnopharmacol 2014;151:78-92.
Zhu MQ, Wen JL, Su YQ, Wei Q, Sun RC. Effect of structural changes of lignin during the autohydrolysis and organosolv pretreatment on Eucommia ulmoides
Oliver for an effective enzymatic hydrolysis. Bioresour Technol 2015;185:378-85.
Zhang Q, Su Y, Zhang J. Seasonal difference in antioxidant capacity and active compounds contents of Eucommia ulmoides
Oliver leaf. Molecules 2013;18:1857-68.
Horikawa T, Kitakaze Y, Sekida T, Hayashi J, Katoh M. Characteristics and humidity control capacity of activated carbon from bamboo. Bioresour Technol 2010;101:3964-9.
Teraoka F, Hamada Y, Takahashi J. Bamboo charcoal inhibits growth of HeLa cells in vitro
. Dent Mater J 2004;23:633-7.
Zhenchao J, Yuting Z, Jiuming Y, Yedan L, Yang S, Jinyao C, et al.
Safety assessment of dietary bamboo charcoal powder: A 90-day subchronic oral toxicity and mutagenicity studies. Food Chem Toxicol 2015;75:50-7.
Ye TT, Xu W, Shi TY, Yang R, Yang XG, Wang XG, et al
. Targeted delivery of docetaxel to the metastatic lymph nodes: A comparison study between nanoliposomes and activated carbon nanoparticles. Asian J Pharm Sci 2015;10:64-72.
Wang LY, Zhang H, Cao JP, Zhang WF, Zhao HL, Yang YS. Effect of activated carbon surface functional groups on nano-lead electrodeposition and hydrogen evolution and its applications in lead-carbon batteries. Electrochim Acta 2015;186:654-63.
Fu Z, Yan L, Li K, Ge B, Pu L, Zhang X. The performance and mechanism of modified activated carbon air cathode by non-stoichiometric nano Fe3O4 in the microbial fuel cell. Biosens Bioelectron 2015;74:989-95.
Lima CF, Costa M, Proença MF, Pereira-Wilson C. Novel structurally similar chromene derivatives with opposing effects on p53 and apoptosis mechanisms in colorectal HCT116 cancer cells. Eur J Pharm Sci 2015;72:34-45.
Stepanenko AA, Dmitrenko VV. Pitfalls of the MTT assay: Direct and off-target effects of inhibitors can result in over/underestimation of cell viability. Gene 2015;574:193-203.
Steinkopf S, Hanekam L, Schaathun M, Budnjo A, Haug BE, Nerdal W. Interaction of local anaesthetic articaine enantiomers with brain lipids: A Langmuir monolayer study. Eur J Pharm Sci 2012;47:394-401.
Reffas A, Bernardet V, David B, Reinert L, Lehocine MB, Dubois M, et al.
Carbons prepared from coffee grounds by H3PO4 activation: Characterization and adsorption of methylene blue and Nylosan Red N-2RBL. J Hazard Mater 2010;175:779-88.
Puziy AM, Poddubnaya OI, Martínez-Alonso A, Suárez-García F, Tascón JM. Surface chemistry of phosphorus-containing carbons of lignocellulosic origin. Carbon 2005;43:2857-68.
[Figure 1], [Figure 2], [Figure 3], [Figure 4], [Figure 5]
[Table 1], [Table 2]
|This article has been cited by|
||Preparation of Phenylalanine-Based Polyesteramide Nano-Drug Delivery System and Its anti-Prostate Cancer Effect ináVitro
| ||Yong Lan, Xiaolong Xiang, Fu Zheng, Hongbo Chen |
| ||Integrated Ferroelectrics. 2021; 216(1): 122 |
|[Pubmed] | [DOI]|
||Effects of ginsenoside Rb1 on second-degree burn wound healing and FGF-2/PDGF-BB/PDGFR-▀ pathway modulation
| ||Li Zhang, Qin Hu, Haonan Jin, Yongzhao Yang, Yan Yang, Renhua Yang, Zhiqiang Shen, Peng Chen |
| ||Chinese Medicine. 2021; 16(1) |
|[Pubmed] | [DOI]|
||Puerarin Loaded PLGA Nanoparticles: Optimization Processes of Preparation and Anti-alcohol Intoxication Effects in Mice
| ||Qin Han, Kejie Chen, Cunli Su, Xin Liu, Xiaoming Luo |
| ||AAPS PharmSciTech. 2021; 22(6) |
|[Pubmed] | [DOI]|
||Ultrasound-based fractional precipitation for the purification of (+)-dihydromyricetin
| ||Se-Rin Oh, Jin-Hyun Kim |
| ||Korean Journal of Chemical Engineering. 2021; 38(3): 480 |
|[Pubmed] | [DOI]|
||The combination of nanotechnology and traditional Chinese medicine (TCM) inspires the modernization of TCM: review on nanotechnology in TCM-based drug delivery systems
| ||Yinghao Zheng, Yun Wang, Mengyu Xia, Ya Gao, Lan Zhang, Yanan Song, Cun Zhang |
| ||Drug Delivery and Translational Research. 2021; |
|[Pubmed] | [DOI]|
||Interactive effects of mulberry leaf meal and bamboo charcoal additive on growth performance, anti-oxidant capacity, and disease resistance of genetically improved farmed tilapia (GIFT) juvenile (Oreochromis niloticus)
| ||Linghong Miao, Oberu Charles, Yan Lin, Yating Gong, Wenbin Zhu, Lanmei Wang, Jianjun Fu, Zhibin Zhang, Zaijie Dong |
| ||Aquaculture Reports. 2020; 18: 100483 |
|[Pubmed] | [DOI]|
||COMMUNITY BASED TOURISM: REVITALIZATION OF VILLAGES THROUGH BAMBOO PLANTATION CONSERVATION
| ||Suranto ., Budi Eko Soetjipto, Hari Wahyono, Agung Haryono, Shazaitul Azreen Rodzalan |
| ||Humanities & Social Sciences Reviews. 2019; 7(2): 331 |
|[Pubmed] | [DOI]|